[1]陶春虎,刘昌奎.舰载机的腐蚀失效及其预防[J].中国材料进展,2014,(10):011-15.[doi:10.7502/j.issn.1674-3962.2014.09.13]
 TAO Chunhu,LIU Changkui.Corrosion Failure and Prevention of Carrier-based Aircraft[J].MATERIALS CHINA,2014,(10):011-15.[doi:10.7502/j.issn.1674-3962.2014.09.13]
点击复制

舰载机的腐蚀失效及其预防()
分享到:

中国材料进展[ISSN:1674-3962/CN:61-1473/TG]

卷:
期数:
2014年第10期
页码:
011-15
栏目:
特约研究论文
出版日期:
2014-10-31

文章信息/Info

Title:
Corrosion Failure and Prevention of Carrier-based Aircraft
作者:
陶春虎12刘昌奎12
1.北京航空材料研究院,北京 100095,中国;2.航空材料检测与评价北京市重点实验室,北京100095,中国)
Author(s):
TAO Chunhu LIU Changkui
关键词:
舰载机腐蚀失效设计工艺材料
DOI:
10.7502/j.issn.1674-3962.2014.09.13
文献标志码:
A
摘要:
本文介绍了舰载机点蚀、丝状腐蚀、晶间腐蚀、应力腐蚀和氢脆5种常见的腐蚀失效模式及其形成机理、失效现象与特征、影响因素等,列举了与设计、制造工艺、材料等因素相关的导致飞机构件腐蚀失效的典型案例,并根据案例的失效原因提出舰载机腐蚀失效的预防与改进措施,以及在设计、制造工艺和选材方面的一些建议。结果表明,飞机的腐蚀控制是一项系统工程,设计中需要充分考虑对导致腐蚀的因素进行有效控制,并注意细节防腐设计;在选用合理的防腐工艺措施的同时,工艺和材料选择与环境之间,工艺与材料之间在防腐方面均应匹配。
Abstract:
Pitting, filiform corrosion, intergranular corrosion andhydrogen embrittlement are the common corrosion failure modes in the carrier-based aircraft. The formation mechanisms, failure phenomena,failure characteristicsand influencing factors of these five failure modes are introduced in this paper. Several typical cases of corrosion failure which induced by design, manufacturing processes, materialsand otherfactors are presented respectively. The prevention and improvement measures are given, according to the failure reason in each case. Some recommendationsin the design, manufacturing processes and material selections are also discussed here. The results shows that the corrosion control of the aircrafts is a systematic project. In the design, it is necessary to take full account of controlling the factors which affect the corrosion, and pay attention to the details of the anti-corrosion design; In the selection of reasonable anti-corrosion process, the material and process should get a mutual appropriate match, furthermore, the material and its process should adapt to the environment demands.
更新日期/Last Update: 2014-09-25