Design, Development and 3D Printing of Biodegradable Poly(Oxime Urethane) Material
文章编号:
1674-3962(2023)04-0314-06
作者:
吴琪琳1; 陈闻一1; 2; 游正伟1; 2
1. 东华大学材料科学与工程学院 纤维材料改性国家重点实验室，上海 201600 2. 功能材料研究中心 中国纺织工程学会柔性电子生物医用纺织材料科研基地 上海纳米生物材料与再生医学工程技术研究中心，上海 201600
Author(s):
WU Qilin1;  CHEN Wenyi1; 2;  YOU Zhengwei1; 2
1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201600, China 2. Shanghai Engineering Research Center of Nano-Biomaterials and Regenerative Medicine,Research Base of Textile Materials for Flexible Electronics and Biomedical Applications,China Textile Engineering Society, Institute of Functional Materials, Shanghai 201600, China
关键词:
聚氨酯; 聚己内酯; 可降解; 3D打印; 生物医用材料
Keywords:
polyurethane;  polycaprolactone;  biodegra-dable;  3D printing;  biomedical materials
分类号:
O633
DOI:
10.7502/j.issn.1674-3962.202202016
文献标志码:
A
摘要:
针对生物医学应用，研制了一种新型的具有良好降解性和可3D打印的聚氨酯材料——聚肟氨酯。通过聚己内酯二醇、丁二酮肟和异佛尔酮二异氰酸酯的两步缩聚反应制备得到了可降解的聚己内酯基聚肟氨酯材料（PCL-PU）。利用傅里叶变换红外光谱、核磁共振氢谱、凝胶渗透色谱分析、热重分析、差示扫描量热法、流变学测试、体外酶促降解实验、单轴拉伸试验和压缩试验等分析测试方法对PCLPU的分子结构和性能进行了表征。研究结果表明，成功合成了聚己内酯基聚肟氨酯材料，该材料具有良好的热稳定性、可降解性和力学性能，体外降解7 d后该材料的降解率可达（44.3±12.9）%。同时，PCL-PU具有良好的加工性能，在99 ℃时可方便快捷地3D打印。该材料有望应用于组织工程支架等生物医学领域。
Abstract:
A novel polyurethane material—poly(oxime urethane), which with good degradability and 3D printing ability, was developed for biomedical applications. The biodegradable polycaprolactone based poly(oxime urethane) (PCL-PU) was synthesized by two-step polycondensation of polycaprolactone diol, isophorone diisocyanate and dimethylglyoxime. The structure and properties of PCL-PU were characterized by Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance (1H-NMR), gel permeation chromatography (GPC), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), rheological measurement, enzymatic degradation test, uniaxial tensile test and compression test. The results showed that PCL-PU was successfully synthesized. PCL-PU possessed good thermal stability, degradability and mechanical properties. After degradation for 7 d, the degradation rate of PCL-PU reached (44.3±12.9)%. At the same time, PCL-PU possessed good processibility and could be readily 3D printed at 99 ℃. This material was expected to be applied in the field of biomedicine such as tissue engineering scaffolds.

参考文献/References:

\[1\]TOFAIL S A M, KOUMOULOS E P, BANDYOPADHYAY A, et al. Materials Today\[J\], 2018, 21(1): 22-37. \[2\]FARAHANI R D, DUBE M, THERRIAULT D. Advanced Materials\[J\], 2016, 28(28): 5794-5821. \[3\]SARANTI A, TIRONSTATHOPOULOS A, PAPAIOANNOU L, et al. Smart Materials in Medicine\[J\], 2022, 3: 12-19. \[4\]LEI F, LIANG M H, LIU Y, et al. Advanced Fiber Materials\[J\], 2021, 3(6): 383-393. \[5\]毛宏理, 顾忠伟. 中国材料进展\[J\], 2018, 37(12): 949-969. MAO H L, GU Z W. Materials China\[J\], 2018, 37(12): 949-969. \[6\]LARRAZA I, VADILLO J, CALVOCORREAS T, et al. Polymers\[J\], 2021, 13(5): 839. \[7\]SANTERRE J P, WOODHOUSE K, LAROCHE G, et al. Biomaterials\[J\], 2005, 26(35): 7457-7470. \[8\]YAO Y, XIAO M, LIU W. Macromolecular Chemistry and Physics\[J\], 2021, 222(8): 2100002. \[9\]ROTH Y, DAN Y L. Polymers\[J\], 2020, 12(5): 1131. \[10\]ASADPOUR S, AI J, DAVOUDI P, et al. Biomedical Materials\[J\], 2018, 13(3): 035007. \[11\]IGA C, AGATA T, MARCIN L, et al. Polymers\[J\], 2020, 12(1): 171. \[12\]WEN Y T, DAI N T, HSU S H. Acta Biomaterialia\[J\], 2019, 88: 301-313. \[13\]LIU Z H, ZHANG L Z, GUAN Q B, et al. Advanced Functional Materials\[J\], 2019, 29(28): 1901058. \[14\]ZHANG L Z, LIU Z H, WU X L, et al. Advanced Materials\[J\], 2019, 31(23): e1901402. \[15\]GAO H, XU J N, LIU S, et al. Journal of Colloid and Interface Science\[J\], 2021, 597: 393-400. \[16\]WANG S L, LIU Z H, ZHANG L Z, et al. Materials Chemistry Frontiers\[J\], 2019, 3(9): 1833-1839. \[17\]ZHANG L Z, YOU Z W. Chinese Journal of Polymer Science\[J\], 2021, 39(10): 1281-1291. \[18\]JIANG C Y, ZHANG L Z, YANG Q, et al. Nature Communications\[J\], 2021, 12(1): 4395.

备注/Memo

备注/Memo:
收稿日期：2022-02-15修回日期：2022-08-29 基金项目：国家自然科学基金资助项目（52173117）；上海市 自然科学基金项目（20ZR1402500） 第一作者：吴琪琳，女，1970年生，教授，博士生导师 通讯作者：游正伟，男，1978年生，教授，博士生导师， Email:zyou@dhu.edu.cn
更新日期/Last Update: 2023-03-22