超疏水表面微纳结构设计与制备及润湿行为调控(Ⅱ)
分享到:

中国材料进展[ISSN:1674-3962/CN:61-1473/TG]

卷:
期数:
2010年第2期
页码:
031-44
栏目:
前沿综述
出版日期:
2010-04-25

文章信息/Info

Title:
Superhydrophobic Surfaces:Design and Fabrication of Micro/Nanomicrotextures and the Tuning of Wetting Behavior(Ⅱ)
作者:
崔晓松1姚 希2刘海华1方国平1李 文1江雷2
(1湘潭大学材料与光电物理学院 低维材料及其应用技术教育部重点实验室,湖南 湘潭 411105)
(2中国科学院化学研究所 有机固体重点实验室,北京 100190)[
Author(s):
CUI XiaosongYAO XiLIU HaihuaFANG GuopingLI WenJAING Lei
(1Key laboratory of Low Dimensional Materials and Application Technology (Ministry of Education) and Faculty of 
Materials and Optoelectronic Physics,Xiangtan University,Hunan Xiangtan 411105,Chin.)
(2State Key Laboratory of Organic Solids,Institute of Chemistry,Chinese Academy of Sciences,Beijing 100080,China)
关键词:
超疏水接触角接触角滞后几何设计制备方法
文献标志码:
A
摘要:
超疏水表面因其优异的自洁排水性能可望在高科技领域和日常生活等方面有美好的应用前景。目前通过对荷叶表面微纳结构仿生已达到在亲水材料上制备超疏水表面的准商业化水平。然而,超疏水表面现有制备方法一般都工艺复杂和费用高昂,同时其超疏水性与其他材料性能很难相容,限制了其实际应用。对此,特别需要深入理论研究,优化设计表面微纳结构,同时充分利用外界作用调控其润湿行为,实现其在某些高科技领域的率先应用。针对超疏水表面研究的这些关键问题,重点评述了当前超疏水表面理论研究特别是表面几何设计方面的最新进展,总结了目前国内外制备超疏水表面的流行技术方法,进而讨论了利用外界作用调控超疏水行为的可能性。