多芯MgB2/NbZr/Cu线材的制备及性能研究
中国材料进展[ISSN:1674-3962/CN:61-1473/TG]
- 卷:
-
- 期数:
-
2009年第4期
- 页码:
-
023-27
- 栏目:
-
特约研究论文
- 出版日期:
-
2009-04-25
文章信息/Info
- Title:
-
Fabrication and Properties of Multifilamentary MgB2/NbZr/Cu Wires
- 作者:
-
闫果1; 王庆阳1; 刘国庆1; 熊晓梅1; 冯勇1; A. Sulpice2; E. Mossang3
-
(1西北有色金属研究院,陕西 西安710016)
(2Institut NEEL/CNRSUJF, B.P. 166, 38042 Grenoble Cedex 9, France)
(3LCMI/CNRS, B.P. 166, 38042 Grenoble Cedex 9 , France)
- Author(s):
-
YAN Guo1; WANG Qingyang1; LIU Guoqing1; XIONG Xiaomei1; FENG Yong1; Sulpice A2; Mossang E3
-
(1Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China)
(2Institut NEEL/CNRSUJF, B.P. 166, 38042 Grenoble Cedex 9, France)
(3LCMI/CNRS, B.P. 166, 38042 Grenoble cedex 9 , France)
-
- 关键词:
-
多芯MgB2线材; 元素掺杂; 粉末装管法; 临界电流密度
- 文献标志码:
-
A
- 摘要:
-
采用NbZr/Cu复合管作为外包套材料,用粉末装管工艺(PIT)制备出千米级TiC掺杂的多芯MgB2/NbZr/Cu线材。在流动高纯氩气保护下、650~800 ℃温度区间内烧结2 h。微观结构分析显示,该工艺制备的MgB2/NbZr/Cu线材具有良好的晶粒连结性和较高的致密度。采用标准的四引线法,在4.2 K不同磁场下测试线材的临界电流密度,在10 T时,线材临界电流密度Jc达到18×104 A/cm2。