[1]王玲,吴浩,管学茂,等.应力-化学介质-冻融循环协同作用下水泥基材料失效机理及寿命预测的研究[J].中国材料进展,2010,(9):025-33.
WANG Ling,WU Hao,GUAN Xuemao,et al.Research on Failure Mechanism and Service Life Prediction of High Performance Cementitious Materials under the Synergistic Effect of Stress,Chemical Medium and Freezing Thawing Cycle[J].MATERIALS CHINA,2010,(9):025-33.
点击复制
应力-化学介质-冻融循环协同作用下水泥基材料失效机理及寿命预测的研究(
)
中国材料进展[ISSN:1674-3962/CN:61-1473/TG]
- 卷:
-
- 期数:
-
2010年第9期
- 页码:
-
025-33
- 栏目:
-
特约研究论文
- 出版日期:
-
2010-10-26
文章信息/Info
- Title:
-
Research on Failure Mechanism and Service Life Prediction of High Performance Cementitious Materials under the Synergistic Effect of Stress,Chemical Medium and Freezing Thawing Cycle
- 作者:
-
王玲; 吴浩; 管学茂; 黄鹏飞
-
中国建筑材料科学研究总院 绿色建筑材料国家重点实验室,北京 100024
- Author(s):
-
WANG Ling; WU Hao; GUAN Xuemao; HUANG Pengfei
-
State Key Laboratory of Green Building Materials,China Building Materials Academy,Beijing 100024,China
-
- 关键词:
-
失效机理; 寿命预测; 化学介质; 水泥基材料; 冻融循环
- 文献标志码:
-
A
- 摘要:
-
针对水泥基材料在应力-化学介质-冻融循环协同作用下的耐久性进行了研究,并开发了多种材料失效试验方法和装置。砂浆试件应力-化学腐蚀协同作用试验装置的特点是加载稳定,克服了应力松弛;协同作用耐久性试验装置可以用于监测协同作用下钢筋混凝土试件性能的衰减过程。研究发现:矿物掺合料改善抗渗性的能力依次是矿渣粉、活化煤矸石粉、粉煤灰;随应力比加大和冻融循环次数增加,水泥基材料中钢筋锈蚀加速、化学介质的渗透速度和深度增大,协同作用加速了水泥基材料的失效;可以用一元二次函数来近似预测氯盐-冻融循环-弯曲荷载协同耦合作用下的寿命。