1200 MPa 级新型高强韧钛合金
()
分享到:

中国材料进展[ISSN:1674-3962/CN:61-1473/TG]

卷:
期数:
2016年第12期
页码:
041-45
栏目:
研究报告
出版日期:
2016-12-31

文章信息/Info

Title:
New High Strength and High Toughness Titanium Alloy with 1200 MPa
作者:
赵永庆马朝利常 辉辛社伟周 廉
西北有色金属研究院,北京航空航天大学,南京工业大学
Author(s):
ZHAO Yongqing MA Chaoli CHANG Hui XIN Shewei ZHOU Lian
Northwest Institute for Nonferrous Metal Research,Beihang University,Nanjing Tech University
关键词:
高强韧钛合金成分设计组织力学性能
DOI:
10.7502/j.issn.1674-3962.2016.12.05
文献标志码:
A
摘要:
随着飞机结构件用钛量的大幅度增加,对钛合金的性能要求也随飞机设计概念的改变而改变,在追求钛合金高强度的同时,也要求合金具有高的韧性。为设计一种强度高于1200 MPa、断裂韧性大于65 MPa·m1/2的新型高强高韧钛合金,在计算合金Mo当量的基础上,合金设计时综合考虑了合金元素对α相、β相的强化和韧化的影响,以及微观组织对强韧性的影响,设计获得一种新型高强高韧富β型的钛合金Ti-5321。实验室条件下30 kg铸锭和中试条件下500 kg铸锭试制的棒材在较理想的显微组织下,新设计的合金室温抗拉强度大于1200 MPa、延伸率大于8%、断裂韧性大于65 MPa·m1/2,相比于现有高强高韧钛合金,显示出明显优势。
Abstract:
Ti usage in airplane is obviously increasing, the requirements for Ti-alloys are changing to high strength and high toughness with the changing of airplane design concept. In order to design a new Ti-alloy with tensile strength over 1200 MPa and fracture toughness over 65 MPa·m1/2, the following factors should be paid attention to: Mo equivalent, effects of alloying elements and microstructures on strength and toughness of α phase and β phase. A new Ti alloy named as Ti5321 was designed, which is a rich-β alloy. Bars were forged from 30 kg and 500 kg ingots. With the ideal microstructure, the bars of the new alloy have a good match between strength and toughness, that is , tensile strength over 1200 MPa, elongation over 8% and fracture toughness over 65 MPa·m1/2. Compared with the TC21, Ti-5553 and Ti-55531 alloy, the new alloy possesses obvious advantages. 